A domestic carbon fiber cloth
Tensile strength: more than 3400MPA
Tensile rate: more than 1.7%
Modulus of elasticity: more than 240000MPA
Thickness: 300g / M2 0.167mm.
200g / M2. 0.111mm
Width: General 10CM, 20CM, 30CM, 50CM
Length: Standard 100M
Features
High strength, low density, thin, substantially increasing the weight of the reinforcing member and the cross-sectional dimensions. Wide application, widely applicable to various types of building bridges, tunnels and other structures, structural repair and reinforcement of structural shapes of seismic strengthening and reinforcing node. Convenient construction, no large-scale machinery equipment, no wet work, no flare, no fixed-site facilities, the construction occupies little space, high efficiency construction. High durability, due not rust, is very suitable for high-acid, alkali, salt and atmospheric corrosion environment.
Scope
For a variety of structural types, various structural reinforcement repair parts, such as beams, plates, columns, roof trusses, piers, bridges, tube, shell and other structures. Suitable for reinforcement and seismic reinforcement work of reinforced concrete structure, masonry structure, wood structure, especially for complex surfaces and forms such as structure node port engineering and water conservancy and hydropower. Grass-roots strength of concrete demands not less than C15. The environmental temperature in the range of 5 ~ 35 ℃, relative humidity less than 70%.
Process principles
Consolidation principle is carbon fiber, high-performance carbon fibers impregnated with resin supporting member of glue to the surface of the concrete, the use of carbon fiber material good tensile strength, achieve the purpose of reinforcing members carrying capacity and strength.
Instructions
Strengthened by CFRP construction points:
Unloading the substrate processing → → → bottom leveling glue stick → → protection
- 2016-04-01What is carbon fiber?
- 2016-03-10Carbon fiber structure composed of what?
- 2016-02-18Analysis of the physical properties of carbon fibe
- 2016-01-20Chemical properties of carbon fiber you know?
- 2015-12-03Overview of the carbon fiber process